| Indicators | Curing agent 6807 A | Resin agent 6807B |
| Appearance | Brown Liquid | Black Liquid |
| Viscosity (CPS) | 100±40 | 4000±1200 |
| Mixed viscosity (CPS) | 1100±300 |
| Density (g/cm³ .25℃) | 1.21±0.05 | 1.52±0.05 |
| Usage ratio (weight ratio) | A:B=20:100 |
| Pot life 100g (min. 25 ℃) | 30±5 |
| Curing conditions | Room temperature curing or heating curing |
| Gel time (min.25 ℃) | 90-120 |
| Color (after curing) | Black |
| Hardness (ShoreA/D) | 85±5A |
| Curing time（23~25℃） | 5-8H |
| Curing time (Heating) | 80 ℃ for 20 minutes |
| Temperature resistance (℃) | -40℃~130℃ |
| Water absorption (24H) | ≤0.5% |
| Anti-UV Grade（GB/T14522-2008） | / |
| Thermal conductivity (W/m.k) | 0.6 |
| Dielectric Strength (kV/mm) | ≥20 |
| Surface Resistivity (Ω/sp) | 1.88×1015 |
| Volume resistivity (Ω.cm) | 1.25×1014 |
| Flame retardant (UL94) | V0 |
| Dielectric constant (1K Hz) | 4.6 |
| Tensile strength (MPa) | ≥3 |
| Ultimate elongation (%） | ≥45% |
| Average coefficient of linear expansion | 149×10-6K-1 |
| Electrification index (CTI) | Ⅰ/600V |